Method to prepare concrete mixture to manufacture ballast pipe and device for previous preparation of concrete mixture tempering water. RU patent 2453515.

FIELD: construction.

SUBSTANCE: method to prepare a concrete mixture for manufacturing of a ballast pipe includes mixing of a sulfate-resistant portland cement, heavy spar ore, a plasticising additive on the basis of polycarboxylate ether and water at the following ratio of the components, in wt %: sulfate resistant portland cement 12 -17, water 4-10, plasticising additive on the basis of polycarboxylate ether 0.1- 0.25, heavy spar ore - balance, at the following content of heavy spar ore fractions in wt %: coarse 3-25 mm 7 - 18, fine 0.16 mm - 3 mm 70 - 85, very fine 0.01-0.16 mm 7 - 16, and tempering water of the concrete mixture is previously processed, sending through the magnetic field, where intensity is maintained with the value of 120000 -140000 A/m, with the speed of 0.5 -3.0 m/s, at the same time the water treatment time makes at least 2 hours. The device for preliminary treatment of the concrete mixture tempering water for manufacturing of a ballast pipe comprises a reservoir for water storage, with inlet and outlet nozzles, and a unit of tempering water treatment, the outlet nozzle of the reservoir is connected with the inlet of the tempering water treatment unit arranged in the form of a hollow extended element, inside of which there is permanent magnet with formation of a gap with the inner wall of the hollow extended element, the value of which makes 3 -5 mm, at the same time the permanent magnet has the intensity of the magnetic field of 120000 -140000 A/m, the outlet of the tempering water treatment unit is connected to the inlet nozzle of the reservoir, the outlet of the tempering water treatment unit is connected with the inlet nozzle of the reservoir, the reservoir has an opening for water draining. The invention is developed in subclaims of the invention formula.

EFFECT: higher density of a concrete mixture and production of a concrete with increased strength.

6 cl, 2 tbl, 2 dwg

IPC classes for russian patent Method to prepare concrete mixture to manufacture ballast pipe and device for previous preparation of concrete mixture tempering water. RU patent 2453515. (RU 2453515):

F16L58/06 - by cement, concrete, or the like

C04B28/02 - containing hydraulic cements other than calcium sulfates

C04B111/20 - LIME; MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS (devitrified glass-ceramics C03C0010000000); REFRACTORIES (alloys based on refractory metals C22C); TREATMENT OF NATURAL STONE

Another patents in same IPC classes:

Method of pipeline coating and device for implementation thereof / 2451870
Device comprises chambers with sleeves ends of which are unbent and fixed on the perimetre of the pipeline. Cavities formed by the unbent sites of the sleeves are connected with fluid agent supply systems. The drums are mounted out of a longitudinal axis of the pipeline. One end of the sleeve is fixed on the perimetre of the pipeline, while the second end of the sleeve is connected through hoisting slings with a flexible coupler an end of which is connected with a traction organ. The device is supplied with a pipe stopper represented in the form of a torus mounted on the pipe connected to a hollow cylinder. The device may comprise an additional chamber with a sleeve an end of which is fixed on the perimetre of the pipeline, while the second end of the sleeve is connected through hoisting slings with a flexible coupler connected to the traction body.

Ballast material for under water mains / 2437020
Ballast material for under water mains contains cement, filler, plasticiser and water. As cement there is used sulphate resistant Portland cement; as a plasticiser there is used poly-carbonate PCE, and as filler there is used barite industrial product, barite ore and iron-manganese concentrate. Material has the following ratio of components, wt %: Portland cement - 8.2-10.5, water - 5.2-6.7, plasticiser - 0.1-0.15, barite industrial product - 18-28 with density 3.78-3.82 kg/cm3 and humidity 0.9-2.1 %, barite ore - 18-28 with density 3.9-4.1 kg/cm3 and humidity 2 %, and iron-manganese concentrate - 25-45 with density 4.2-4.5 kg/cm3 and humidity 4 %. Ratio of water to Portland cement is 035-0.5. Components of filler have the following granulo-metric composition: 0-0.16 cm - to 5 %, 0.16-1.0 cm - to 25 %, 1.0-2.5 cm - to 35 % and 2.5-5.0 cm - the rest.

Procedure for manufacture of sulphate resistant heavy-weight pipe / 2435094
Procedure for manufacture of sulphate resistant heavy-weight pipe consists in covering central pipe with concrete coating. Concrete mixture with fluidity 4-8 cm by Cone of Abrams, made of sulphate resistant Portland cement m500, water, super-plasticiser, water repellent agent and barite or ore, is applied by spraying. Also, first there is sprayed the first layer of thickness a, further there is wound a reinforcing fibreglass net and the second layer is sprayed consisting of concrete mixture of thickness (0.5-1.5)a with shear between a zone of winding and zone of spraying at 1-3 m. Further, the pipe is left on a rack, till concrete mixture stiffens. A pipe is conditioned in a storage for not less, than three days to facilitate storage strength.

Procedure for preparing ballast material for underwater pipeline / 2412393
Procedure for preparing ballast material for underwater pipeline consists in mixing cement, filler, water and plasticiser to make mixture of specified density and flowability. As plasticiser there is used filler of big dimension from the group: barite or iron containing ore or their mixture. Also, mixing is carried out in two stages. At the first stage 10-20 wt % of said big dimension filler of its total amount is supplied into the mixer together with cement, water and plasticiser and mixed for 10-15 sec. At the second stage the rest filler of big dimension is supplied in equal batches with intervals of 10-15 sec, and it is mixed; the components are mixed till there is obtained a homogenous mixture.

Ballast material / 2399828
Ballast material contains cement, filler and water; as ballast it contains barium ore of big fractions with dimension of grains over 5 mm to 25 mm, of small fractions with dimension of grains over 0.16 mm to 5 mm, of super fine fractions with dimension of particles from 0.01 mcm to 160 mcm and additionally plasticiser-poly-carboacetyl at the following ratio of components in wt %: cement 12-17, water -10, poly-carbo-acetyl 0.2-0.3, barium ore - the rest at the following contents of fractions in ore wt %: big fraction over 5 mm to 25 mm 8-16, small fraction over 0.16 mm to 5 mm 70-84, super fine fraction over 0.01 mcm to 160 mcm 8-14.

Method of manufacture and connection of pipes with internal cement-sand coating / 2398156
Thin-walled bushings out of corrosion resistant metal are positioned inside ends of pipes so, that external ends of bushings project beyond ends of pipes; projecting ends of bushings are flanged on ends of pipes; bushings are fixed by mutual calibration of bushings and pipe ends by internal diametre; coating is applied and prepared ends of pipes are butt-welded according to process of two-layer metal weld.

Method of pipeline rehabilitation, mobile repair complex for rehabilitation and pipeline covering equipment / 2324103
In the repair method, the pipeline trench which also work as formwork for the construction of new pipes, after placement of earth backfill, successive layers of loading bearing materials, either smooth or with longitudinal reinforcement and a cover layer are placed. An S-shaped fitting joint, with an elastic shell inside it, is mounted onto the pipe entrance, and an alluvial chamber pipe, with a spatula shell, is fitted onto the fitting. After this, polymer cement concrete "ФОРТ" is injected onto the space between the shells. When placing the loading bearing layers with longitudinal reinforcement, the spatula shell, which is equipped by a profile cuff is used to make lateral furrows on the earth backfill. After the layer sets up, the spatula shell, starting from the smooth edge, is used to place load bearing layer of poly cement "ФОРТ" with a high content of poly-acryl, carbon plastic or metallic fibres in the furrow and these forms longitudinal reinforcement. A rehabilitated pipeline contains a proper repaired pipe, backfill layers of load bearing materials, smooth or with longitudinal reinforcement, placed between layers of soil backfills and protective cover of polymer-cement "ФОРТ". These layers have different composition depending on the intended purpose of the whole system of the new pipe. Apart from this, the solution fall into the mobile repair complex for its repairs and equipment for covering pipelines.

Fine-grained concrete composition for protective coat of pipe inner surfaces / 2299187
Proposed composition is used for pipes at large curvature of walls (inner diameter of 100-400 mm) which are used in erection of water supply systems, both for potable water and other non-aggressive aqueous media. Proposed concrete composition includes Portland cement ПЦ500-ДО, bank-run sand of 0.063-2 mm fraction and M= 1.55-1.9, potassium permanganate and superplasticizing agent C3 and/or modifying agent Linamix 73P-1 or Relamix and water at the following ratio of components, mass-%: Portland cement, 31.25-33.51; bank-run sand, 50.0-53.266; potassium permanganate, 1.67·10-5-5.87·10-5; superplasticizing agent C3, 0.09-1.06; C3 and linamix 73P-1, 0.09-1.06; Linamix 73P-1,0.0840.13; Relamix, 0.067-0.146; the remainder being water. Fine-grained concrete composition may additionally contain up to 3.2 mass-% of dry complex additive with sand of 0.05-0.16 mm fraction, Portland cement and superplasticizing agent at ratio of 2.24 : 0.95 : 0.01. Coats made from such composition acquire enhanced early flexural and compressive strength 3-4 h after heat and moisture treatment and final strength after 28 days of treatment.

Method of applying cement-sand coating on outer side of pipe / 2273791
Method comprises cleaning the outer side of the pipe, applying the polymeric insulating material on the outer side of the pipe, and setting the tips in the end sections of the pipe. The tips are made of a corrosion-resisting material, and the inner surface of the tips is conical. The smaller base of the tip faces the pipe end. The coating is applied uniformly and thickened by the forced vibration of the cementing head with the use of vibrator.

Composition for producing construction materials / 2447036
Invention relates to compositions based on mineral binding materials, such as portland cement, and can be used in the industry of construction materials when making concrete, fibre concrete, cement-fibre construction materials, roofing slate, plaster, finishing coats and stucco moulding. The composition for producing construction materials contains cement, sand, water and carbon material. The carbon material used is an aqueous suspension of cavitational-activated carbon-containing material which contains multilayer carbon nanostructures with layer spacing of 0.34-0.36 nm and particle size 60-200 nm, polydispersed carbon tubular formations with dimensions of 10-6-10-5 m, hydrogenated carbon fractal structures with dimensions of 10-8-10-5 m and active loose carbon with graphite defective microcrystals with dimensions of about 10 Ǻ.

Concrete mixture / 2446123
Invention relates to preparation of concrete mixtures for making construction articles and structures.The concrete mixture, which contains cement, crushed cement clinker as coarse and fine aggregate and water, contains said coarse aggregate fraction of 10-40 mm, with the following ratio of components in wt %: cement 20.0-25.0, said coarse aggregate 22.0-28.0, said fine aggregate 28.0-37.0, water 20.0-25.0. The cement used can be cement obtained by grinding said cement clinker which is used as coarse and/or fine aggregate.

Application of rheological additive during vibration compaction treatment of water-based composition and hydraulic binder and produced composition / 2443649
Application of a rheological additive in the method of vibration compaction treatment of a composition containing water and at least one hydraulic binder, which is an emulsion of at least one non-structured copolymer, formed by the following: a) (methyl) acrylic acid; b) alkyl(meth)acrylate, containing from 1 to 25 atoms of carbon, preferably from 1 to 4 carbon atoms, besides, this alkylmethacrylate preferably is ethyl(meth)acrylate; c) monomer of formula R1-(R2O)m-R3, where: - R1 is a radical, containing an unsaturated functional group, capable of polymerisation and included into a vinyl row group or to a group of acryl, methacrylic and maleic esters, or to a group of unsaturated urethanes, such as acryl-urethane, methyl-acryl-urethane, α,α'-dimethylisopropenylbenzylurethane, allyl urethane, or to a group of substituted or non-substituted allyl or vinyl ethers, or also to a group of unsaturated amides or imides of ethylene row, or also to a group made up by acrylamide and methyl-acrylamide, and preferably stands for a methacrylic group; - R2O stands for an alkylene-oxide group containing from 1 to 6 carbon atoms, preferably an ethylene oxide and propylene oxide group and more preferably an ethylene oxide group; - m is an integer number in the interval from 20 to 30, preferably in the range from 23 to 27 and is more preferably equal to 25; - R3 stands for a linear or a ramified alkyl chain containing from 28 to 33 carbon atoms, preferably from 30 to 33 carbon atoms and more preferably containing 32 carbon atoms. The specified additive is used in the composition that contains water and at least one hydraulic binder, and also the specified rheological additive.

Concrete mixture / 2433973
Present invention relates to a concrete mixture and can be used in the industry of construction materials. The concrete mixture contains the following in wt %: cement 9.8-30.0, a modifying additive 0.0-15, water 0.2-25.0, aggregate - the rest up to 100. The aggregate contains the following in wt %: gas purification wastes from thermal treatment of solid household wastes 1.0-50.0, crushed rock 0.0-50.0, screenings 0.0-50.0, sand 0.2-50.0, gravel 0.0-50.0, ash-slag wastes from thermal treatment of solid household wastes - the rest up to 100.

Mixture of substances used particularly as additive for concrete mixture / 2433096
Present invention relates to a mixture of substances used as an additive for curable construction materials, particularly concrete mixture. The mixture of substances used as an additive for curable materials, particularly concrete mixture, contains the following in wt %: xanthan resin 1-8, pseudo-viscous thickener containing water 1-6, thinner 2-10, synthetic resin compatible with cement 20-50, foaming agent 0.1-3, curing accelerator 30-70, preserving agent 0.2-4, wherein the full weight of all components of the mixture of substances must be equal to 100 wt %. Use of said mixture of substances for concrete mixture containing 0.01-0.5 kg preferably 0.05-0.1 kg per kg of the cement of mixture of substances, cement and aggregate. Said concrete mixture contains aggregate in form of any type of sand, any type of soil, dirty or clean, and/or such materials as bauxite, laterite, volcanic ash, pumice and ash from combustion installations. The invention is developed in subclaims.

Mix for production of artificial rock / 2430049
Mix for production of artificial rock contains the following components, wt %: colour cement 25-29; sand on the basis of calcium carbonate 11-15; copper sulfide 1-2; ground swollen schungite of fraction 10-20 mm 27-30; superplasticiser S-3 1.4-2; water - balance.

Mix for production of material with high water absorption / 2430048
Mix for production of material with high water absorption includes the following components, wt %: swollen perlite sand 30-32, gypsum binder 16-20, palygorskite 20-26, water 26-30.

Mortar / 2428391
Invention relates to mortar and can be used to make plaster, in brick laying and in tile joining layers. The mortar contains the following in wt %: cement 21.0-21.9, fine aggregate - quartz sand 58.7-59.3, finely ground filler - finely ground dunite 4.2-4.3, sodium sulphate 0.6-1.5, water - the rest.

Binding composition, construction composition containing said binding composition, method of preparing construction composition and use thereof / 2427547
Present invention relates to a binding composition, a construction composition containing said binding composition, a method of preparing said construction composition and use thereof. The binding composition contains: a) sol in amount of 30.0-70.0% of the total weight of the binding composition; b) an additional composition in amount of 0.1-5.0% of the total weight of the binding composition, wherein the additional composition contains one or more components from group (b1) and one or more components from group (b2), where group (b1) consists of metal chlorides and group (b2) consists of silicon dioxide, zeolite and apatite, wherein one or more of components from group (b1) accounts for 70.0-99.0% of the total weight of components (b1) and (b2), and one or more components from group (b2) account for 1.0-30.0% of the total weight of components (b1) and (b2), c) cement in amount of 25.0-69.9% of the total weight of the binding composition. The construction composition contains said binding composition and a basic component with maximum particle size of 28 mm in amount of at least 15% of the weight of the basic component. The method of preparing the construction composition involves mixing binder and the basic component with water, possibly followed by compaction of the obtained mixture. The construction composition can be used to reinforce soil and making structural elements.

Method of making articles in form of slabs or blocks using acrylic binder / 2421422
Invention relates to a novel method of making articles in form of slabs, porous slabs, blocks made from a conglomerate consisting of pieces of stone. The method is based on the existing technology of compaction by means of vacuum compression and involves preparation of a mixture consisting of a granulate and binder which is an aqueous dispersion of an acrylic prepolymer. The granulate is selected from stone-like materials. The mixture also contains a finely dispersed inorganic aggregate. The mixture is deposited in form of a layer onto a substrate or inside a mould and is compacted via vacuum vibro-compression. Further, the binder which is present in the moulded article is hardened. At the step for compaction using vacuum vibro-compression, the article hardens in conditions which enable to prevent removal of water from the mixture due to evaporation. When making porous slabs, at the compacting step, the article hardens in conditions which enable to remove water from the mixture. When making blocks, the mixture is deposited only inside the mould. When using the method, blocks can also be made, which can then be sawed.

Method to prepare concrete mix on porous filler / 2452714
In the method to prepare a light concrete mixture on a porous filler, including mixing of portland cement with an additive, a porous filler and tempering water, first a superplasticiser additive in the amount of 0.4-0.5% of portland cement mass is added into 50-60% of the total amount of tempering water and mixed with portland cement during 50-60 s, then the whole porous filler is added, such as highly light porous filler with medium density of not more than 250 kg/m3, and again mixed for 70-80 s, afterwards the remaining part of tempering water is added, and the mixture is finally mixed for 30-40 s.

Raw mix to make products / 2452709
Raw mix contains, wt %: cast iron chips 48.0-55.0, graphite 2.0-5.0, gypsum 20.0-25.0, water 20.0-25.0.