RussianPatents.com

Refractory ceramic article. RU patent 2433105.

$Refractory ceramic article. RU patent 2433105.$

FIELD: chemistry.

SUBSTANCE: invention relates to refractory materials and engineering ceramics and can be used in production of refractory ceramic articles, including industrial containers used during synthesis of high-purity materials based on niobiuim and tantalum pentaoxides, as well as for refractory lining of chemical apparatus, furnaces and structural elements. The refractory ceramic article has a base made from several flat blocks of quartz ceramic with moderate porosity, between which there are seams filled with solder of niobium or tantalum pentaoxide, and an outer coating of niobiuim or tantalum pentaoxide applied on the base. The edges of the blocks of the base are rounded and the corners of the blocks are smoothed. The solder in the seams has a double-tee cross-section with concave sides of the support. The width of the seam is not greater than twice the thickness of the block. The spherical radius of the edges of the blocks is not greater than half the thickness of the block.

EFFECT: increase in resistance of the refractory article to thermal shock by 14,6-34% during repeated use in heating-cooling mode, which increases the service life of the refractory article.

2 cl, 2 ex, 2 dwg

IPC classes for russian patent Refractory ceramic article. RU patent 2433105. (RU 2433105):

C04B41/87 - Ceramics

C04B37 - Joining burned ceramic articles with other burned ceramic articles or other articles by heating

C04B35/14 - based on silica

Another patents in same IPC classes:

High temperature coating / 2427559
Invention can be implemented as protection from oxidation of ceramic composite materials for parts of hot routs of perspective gas-turbine installations (GTI) and gas-turbine engines (GTE) of transport systems and power engineering operating under effect of oxidising mediums and fuel combustion products at temperature up to 1600°C. High temperature coating has the following chemical composition, wt %: silicon 10-14, boron 3-7, hafnium oxide 50-60, hafnium boride 12-19, boron carbide 8-14.

Layer or coating and composition for applying said layer or coating / 2394798
Present invention relates to a composition for applying a layer of coating, particularly an anti-adhesion layer for casting moulds which are in contact with molten metals or glass. The composition contains aluminium titanate or silicon nitride with average particle size greater than 500 nm, an oxide inorganic component with average particle size between 100 nm and 10 mcm and a binding agent which contains particles with average size less than 50 nm. When preparing the composition, aluminium titanate or silicon nitride is dispersed in water and the obtained dispersion is mixed with aqueous dispersions of an inorganic oxide component, binding agent and additional components. The oxide component can be aluminium oxide or titanium oxide and the additional components can be boron nitride or graphite. The invention also relates to use of the composition to apply a layer or a coating on fire bricks, graphite or steel articles, to layers or coatings applied from this composition, to articles which are at least coated with the said layer or coating.

Fire-resistant mixture and multicomponent material for protective coatings of heating elements based on lanthanum chromite made from said mixture / 2389709
Invention relates to heat-resistant nonmetallic materials and can be used to make effective protective coatings of heating elements based on lanthanum chromite working in an air atmosphere. The invention involves use of a heat-resistant mixture composed of lanthanum chromite, frits from oxide phases and aluminoborosilicate glass with the following ratio of ingredients, in wt %: lanthanum chromite 32-44, frit 43-48, aluminoborosilicate glass 13-20. The frit from oxide phases contains the following components, in wt %: yttrium oxide Y2O3 63-65, aluminium-magnesium spinel MgAl2O4 13-21, lanthanum aluminate LaAl11O18 6-13, mullite Al6Si2O13 6-13, aluminoborosilicate glass SiO2 53-55, CaO 18-20, Al2O3 13-15, B2O3 9-11, MgO 2-4. The multicomponent material for protective coatings obtained from the mixture contains crystalline phases and a glass phase in the following ratio, in wt %: LaCrO3 29-42, Y2O3 30-31, MgAl2O4 6-8, LaAl11O18 3-5, Al6Si2O13 3-5, aluminoborosilicate glass phase 16-22.

Protective coat / 2383514
Protective coat contains liquid potassium glass and powdery fillers, at the following ratio of components in weight parts: liquid potassium glass - 100-150, silicon carbide - 100-200, graphite - 1-12, sodium fluorsilicate - 0-12.

Method for manufacturing of composite material / 2379268
In manufacturing of a composite material, a carbon-base filling cloth is used as a material blank impregnated with a compound of liquid Bakelite 100 weight fractions, isopropyl alcohol 54-100 weight fractions, tetraethoxysilane 44-160 weight fractions and water 7-32 weight fractions. Thereafter drying, consolidation and thermal processing at temperature 1800-2000°C with formation of silicon carbide follow.

Method of preparing super-hard coated abrasive / 2378231
Described is a method of preparing a super-hard coated abrasive, specifically a coated abrasive based on diamond or cubic born nitride (cBN). When realising this method, an inner layer of an element which is capable of (individually or combined with other elements) forming carbides, nitrides or borides is deposited onto the surface(s) of abrasive material at the first stage through a hot coating method. The hot coating method is selected from a group a group comprising a method of depositing from gaseous phase via thermal decomposition of metal halides, a method of chemical deposition from vapour phase and a thermal diffusion coating method. Vanadium, molybdenum, tantalum, indium, zirconium, niobium, tungsten, aluminium, boron and silicon are usually used for depositing the inner layer. Through reactive sputtering using a reactive gas, the inner layer is coated with at least one outer layer made from material selected from a group comprising metal carbides, metal nitrides, metal borides, metal oxides and carbonitrides, boronitrides and borocarbonitrides of metals, for example carbide or nitride of titanium, silicon or aluminium.

Composition for manufacturing carbon silicon-carbide material / 2375333
Siliconising composition includes the following components, parts by weight: liquid bakelite BZh3 - 100, isopropyl alcohol - 67-100, tetraethoxysilane - 53-160, water - 11-32.

Composition for thermal barrier, machine unit from superalloy with coating containing such composition, ceramic coating and method of coating obtaining / 2365565
Invention relates to composition of ceramic thermal barrier, used in machine units from superalloy. Composition contains base from zirconium oxide, at least one trivalent oxide from group containing erbium oxide, europium oxide, praseodymium oxide, terbium oxide, holmium oxide and their mixtures, allowing to stabilise zirconium oxide and optimally reduce zirconium oxide heat conductivity, and at least one pentavalent oxide from group: niobium oxide, tantalum oxide or their mixture, allowing to reduce number of oxygen vacancies in such way that it was in fact equal to number of oxygen vacancies in partially stabilised zirconium oxide. Said trivalent oxide is present in molar concentration created by the first part, allowing partial stabilisation of zirconium oxide, and by the second part, which introduces point defects into grid, said pentavalent oxide being present in molar concentration equal to molar concentration of said second part of trivalent oxide.

Method of ceramic item engobing / 2356874
Invention concerns ceramic item production, mainly of ornamental purpose. Method of ceramic item engobing involves application of engobing coating onto twisted textile fiber with further fiber positioning fiber onto an item surface, drying and glazing. Twisted textile fiber can be divided in lengthwise sections coated with angobe layer of different colours. Engobing utilises twisted organic textile fiber burned out later during glazing.

Method for processing of fire-resistant products / 2356873
Invention is related to production of fire-resistant products and may be used in aviation and rocket engineering. Technical result is achieved by layerwise saturation of refractory material surface with carbon by means of fullerene solution impregnation in organic dissolvent. Product is placed above heating element so that temperature of saturated surface does not exceed 60-65°C, fullerene solution is supplied in organic dissolvent onto product surface so that complete surface is wetted, and impregnation is carried out for 30-45 minutes.

Joint of metal part with part of ceramic material by soldering / 2432345
Joint comprises a metal part of titanium, aluminium and vanadium or inconel alloy, a part of ceramic material and at least one intermediate element of connection, which is attached by soldering to each of the specified parts. The intermediate element (10') of connection consists of a deformable layer, having at least two flat zones (11, 12), soldered accordingly to each of the specified parts, besides, these two flat zones (11, 12) are connected to each other by a deformable zone (13'), having at least two free waves (19, 20), oriented alternately to the specified metal part and to the specified part from the ceramic material. The part of ceramic material may be formed from a dense silicon carbide or of a composite with ceramic matrix reinforced with carbon fibres.

Assembly of metal part and part made of ceramic material on base of sic or on base of c / 2427555
Assembly of metal part (1) made of alloy on base of nickel or cobalt and part (7) made of ceramic material on base of silicon carbide (SiC) and/or carbon (C) has multi-layer structure including following elements connected by soldering in pairs in following order: metal part (1), first intermediate part (3), second intermediate part (5) and part of ceramic material. Second intermediate part (5) is made of aluminium nitride and/or mullite with expansion coefficient less, than expansion coefficient of material of metal part (1). First intermediate part (3) is fabricated of malleable metal and is capable to deform for compensation of difference of expansion between said metal part (1) and second intermediate part (5).

Soldered joint between titanium-based metal part and part of ceramic material based on silicon carbide (sic) and/or carbon / 2416587
This compound may be used in aviation, in particular, in turbomachine, to connect parts included into the composition of a nozzle, a combustion chamber and an afterburner. The joint comprises a multi-layer structure, which includes the following components joined to each other by means of soldering: a titanium-based metal part (10), the first substrate (11), capable of deformation for adjustment to the difference in expansion of the metal part (10) and a part of ceramic material (20) based on silicon carbide and/or carbon, the second rigid substrate (12) of aluminium (AIN) or tungsten (W) nitride with an expansion ratio that is close to the expansion ratio of the specified part from the ceramic material (20), and the part of the ceramic material (20).

Method for permanently joining articles / 2415822
Invention relates to the metallurgy industry, machine-building and specifically to joining articles made from different or similar material, and can be used in making assembly units in space and aviation engineering, in instrument making, transportation, electronics and other fields. The method for permanently joining articles involves collecting and joining articles in a protective chamber, heating and thermal dissociation of a working mixture, depositing particles formed from the mixture and forming a joining layer from the formed ceramic deposit in the contact area of the articles. The working mixture used is an organosilicon compound - methyl silane, polysilasanes or methylsilasanes, and the ceramic deposit used is silicon carbide, silicon nitride or silicon carbonitride.

Method of obtaining compounds metal-glass, metal-metal and metal- ceramics / 2366040
Invention relates to a method of obtaining glass-to-metal and metal-ceramic compounds and metal-metal compounds used in solid oxide fuel cells. According to the invention, the compounds are obtained by using a mixture of powders of base glass and metal oxide. Adding some components to the glass used in the composite joints, for instance MgO, that influence on its viscosity and wetting ability ensures a local change in the glass properties near the interface with the metal and at the same time making glass bulk properties including increased coefficient of thermal expansion closer to the properties of the other components of the joint.

Method of connecting ceramic units from silicon nitride / 2365564
Invention relates to methods of connecting separate units from silicon nitride, which are used in manufacturing of constructional products, for instance nozzle apparatuses, long thermosteam covers and pipes (chlorine inputs), operating in aluminium melt at temperature 1200°C, glass-melting apparatuses for glass fibre stretching at temperature to 1600°C. Said technical result is achieved by the following: method includes preparing of glue mixture based on silicon nitride, which contains, wt %: 0.5-1.0 - melted magnesium oxide, 0.5-3.0 milted aluminuim oxide, 35-41 aluminiumboronphosphate binding agent and separately - similar mixture with alumochromephosphate binding agent, application on connected surfaces of units first mixture with aluminumboronphosphate binding agent, then mixture with alumochromephosphate binding agent with further coupling of said surfaces. Burning of connected product is carried out at temperature 1000°C with staying for 2 hours.

Method of low-deforming diffusion welding of elements made from sintered non-oxide ceramics and workpiece made from non-oxide ceramics with seamless joint / 2353486
Invention can be used for jointing ceramic elements made from sintered non-oxide ceramics. The elements are brought in contact and jointed by diffusion welding in a low-deforming way, in the presence of protective gas and with a forced applied to form a monolith. Welding temperature makes at least 1600°C, preferably, over 1800°C, most desirable, over 2000°C. The method makes the elements to be jointed subjected to plastic strain less that 5%, and preferably less than 1%.

Pin for sintering of metal ceramic items on cellular stands / 2336147
Pin contains ceramic head and metal rod immersed into it; both are rigid tied to each other by means of high temperature sintering. The ratio of thermal expanding of the head is 1.6-2.8 of thermal expanding ratio of the rod material.

Materials compound, the method of its production and the case for the thyristor activated by light / 2273619
The invention is pertaining to the vacuum-dense and resistant to temperature variations compound of materials made out of alumina sapphire and alumina ceramics and also to the method of its production and its application. Through the first connection layer made out of the manganese-silicate glass, which contains at least one of the following metals: molybdenum, tungsten, palladium or platinum, and the second connection layer made out of the manganese-silicate glass it is possible to produce a durable compound consisting of alumina sapphire and alumina ceramics. The connection layers on the ceramics are formed by the method of the screen-printing of the pastes of the corresponding composition with the subsequent joining of sapphire and burning at the temperature of 1200-1500°C. The indicated compound of the materials is used for insertion of the window made out of the alumina sapphire in the case for the thyristor activated by light.

Method of preparing lightweight proppant and proppant / 2425084
Invention relates to production of ceramic shear proppants meant for use in oil industry as proppants when extracting oil through hydraulic fracturing. The method of preparing a lightweight proppant, involving drying initial components of the mixture, their batching, grinding, granulating the mixture and firing the obtained granules, uses a mixture of the following composition, wt %: quartz-feldspar sand 90.0-97.0, clay and/or kaolin 3.0-10.0, and firing is carried out at heating rate of 350-370°C/h and cooling rate of 800-820°C/h. The mixture is moistened using 2-8% sodium hydroxide and/or potassium hydroxide solution. Components of the mixture are ground to fractions not larger than 40 mcm, with content of the fraction not larger than 5 mcm less than 60 wt %. Said drying is carried out at temperature 200-240°C.

Method of producing solid inorganic material / 2422392
Invention relates to a method of producing solid inorganic material. The method of producing solid mineral material comprises the following steps: a) preparation of an aqueous paste comprising the following steps: a1) preparation of a preliminary paste by reacting (i) powder of one or more materials containing a compound or combination of silicon compounds selected from: silicon compounds which are present in form of anhydrous silicon dioxide (SiO2), selected from amorphous silicon dioxide, quartz, trimidite, crystaballite, stishovite and anhydrous silicon dioxide extracted from plants and silicon compounds present in form of hydrated silicon dioxide (Si(OH)4), selected from diatomite, radiolarite, opal, gaize, flint, sandstone, jasper, agate, chert, lutecite, chalcedonite, quartzine, petrified wood and chalcedony, with (ii) an inorganic base or a combination of inorganic bases, and, if needed, with (iii) addition of water; a2) obtaining a composition containing compounds or combination compounds selected from salts of inorganic acids; a3) obtaining a composition containing an additional mineral or combination of minerals which are crystalline or amorphous, selected from: aluminium silicates; compounds containing aluminium and oxygen; alkaline and alkali-earth carbonates; metal carbonates; silicates containing pure silicon dioxide and alkali-earth silicates; wherein the compositions are selected such that the paste obtained when mixing compositions obtained at step a1), a2) and a3) contain at least (i) silicon in form of anhydrous silicon dioxide, (ii) aluminium and (iii) calcium and/or magnesium; and water; a4) obtaining a paste by mixing compositions from steps a1), a2) and a3); b) moulding the paste obtained at step a); and c) hardening the aqueous paste moulded at step b) by drying at atmospheric pressure and at temperature lower than 99°C until solid inorganic material is obtained. The invention is developed in subclaims.