Charge for glase production |
||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
|
IPC classes for russian patent Charge for glase production (RU 2430039):
Glase / 2430037
Glase contains the following components, wt %: SiO2 14.0-16.0; CaO 1.0-2.0; K2O 4.0-6.0; BaO 1.0-1.5; Al2O3 4.0-6.0; MgO 4.0-6.0; B2O3 59.15-63.25; PbO 4.0-6.0; Cr2O3 0.05-0.1; Fe2O3 0.05-0.1; Na2O 0.5-1.0; SO3 0.05-0.1; TiO2 0.05-0.1.
Tile glase / 2430036
Tile glase includes the following components, wt parts: clay 5-7, quartz sand 70-74, chalk 5-7, soda ash 5-7, cryolite 9-11.
Charge for glase production / 2430035
Charge for glase production contains the following components, wt %: broken window sheet and/or container glass 71-76, kaolin 3-4, soda ash 3-4, nepheline syenite 18 - 21.
Glase / 2430034
Glase contains the following components, wt %: SiO2 45.0-49.0; Al2O3 4.0-5.0; B2O3 4.0-5.0; CaO 4.0-5.0; MgO 4.0-5.0; K2O 4.0-5.0; SnO2 27.0-29.0.
Tin glase / 2430031
Glase includes the following components, wt parts: SiC2 50.0-53.0; SnO2 28.0-30.0; Al2O3 1.0-2.0; CaO 7.0-9.0; MgO 4.0-6.0; Na2O 4.0-6.0.
Glase mixture / 2428401
Invention relates to the technology of silicates and a glase mixture for applying on ceramic tiles and stove tiles. The glase mixture contains the following in wt %: pegmatite 26-30; quartz sand 50-54; borax 6-8; dolomite 1-1.5; calcined soda 2-2.5, boric acid 2-3; bone ash 3-4; alumina 3-4.
Glase / 2428400
Invention relates to glase compositions for coating ceramic tiles, roofing tiles and articles for decorative and art purposes. The glase contains the following in pts.wt: quartz sand 55-57, potash 13-15, soda 13-15, cobalt oxide 0.4-0.6, copper oxide 1.4-1.6, fluorspar 13-15.
Glase / 2428399
Invention relates to a glase composition which can be used in making facade tiles. The glase contains the following in wt %: SiO2 18.35-21.05, CaO 1.0-2.0, K2O 4.0-6.0, BaO 4.0-6.0, Sb2O3 0.2-0.3, Al2O3 4.0-6.0, MgO 4.0-6.0, B2O3 55.0-60.0, Cr2O3 0.05-0.1, Fe2O3 0.05-0.1, Na2O 0.5-1.0, SO3 0.05-0.1, TiO2 0.05-0.1.
Tin glase / 2428387
Invention relates to production of construction materials and may by used for coating of fireplace tile. Glase comprises in wt %: SiO2 - 42.3-49.5; SnO2 25.0-27.0; Al2O3 - 12.0-16.0; CaO - 1.0-1.5; MgO - 4.5-5.5; Na2O - 5.5-6.5; Cr2O3 - 1.5-2.0.
Engobe / 2427558
Engobe contains the following components, wt %: light baked clay 53.0-57.0; quartz sand 16.0-18.0; glass breakage 26.0-28.0; chalk 0.5-1.0. Engobe moisture is 23 - 65 %. Surface of engobed items is even, smooth, without bulging.
Slip for obtainment of glaze coating / 2346900
Invention can be applied in manufacturing of porcelain and faience goods. Glaze slip includes components at the following ratio, wt %: frit 100.0; clay 0.5-1.5; zircon 4.0-5.0; water 40.0-50.0; silica gel 4.0-5.0; barium carbonate 0.7-1.7; sodium chloride 0.1-0.2; sodium tripolyphosphate 0.1-0.2; calcium borate 3.0-4.0. Frit has the following composition, wt %: SiO2 47.0-50.0; ZrO2 4.0-8.0; B2O3 18.0-22.0; MgO 2.0-4.0; K2O 2.8-3.8; F' 0.1-0.2; TiO2 8.0-10.0; BaO 2.0-4.0; ZnO 4.0-8.0.
Mixture for making glaze / 2341471
Proposed mixture for making glaze consists of crushed window and/or container glass, kaolin and titanium slag. The components have the following ratio, in wt %: crushed window and/or container glass 65-75; kaolin 2-4; titanium slag 21-33.
 Colored glaze / 2243173
The invention relates to methods of producing colored glaze, used in production of decorative, utilitarian and economic purposes
 The powder mixture to obtain metal-ceramic coating / 2170714
The invention relates to the creation of defenses of Nickel-based alloys from exposure to aggressive environments, in particular to metal-ceramic coatings used to protect structures of power plants
Mixture for making glaze / 2341471
Proposed mixture for making glaze consists of crushed window and/or container glass, kaolin and titanium slag. The components have the following ratio, in wt %: crushed window and/or container glass 65-75; kaolin 2-4; titanium slag 21-33.
Slip for obtainment of glaze coating / 2346900
Invention can be applied in manufacturing of porcelain and faience goods. Glaze slip includes components at the following ratio, wt %: frit 100.0; clay 0.5-1.5; zircon 4.0-5.0; water 40.0-50.0; silica gel 4.0-5.0; barium carbonate 0.7-1.7; sodium chloride 0.1-0.2; sodium tripolyphosphate 0.1-0.2; calcium borate 3.0-4.0. Frit has the following composition, wt %: SiO2 47.0-50.0; ZrO2 4.0-8.0; B2O3 18.0-22.0; MgO 2.0-4.0; K2O 2.8-3.8; F' 0.1-0.2; TiO2 8.0-10.0; BaO 2.0-4.0; ZnO 4.0-8.0.
Charge for glase production / 2430039
Charge for glase production contains the following components, wt %: broken window sheet and/or container glass 76-82, kaolin 3-4, soda ash 1-2, zircon 8-11, pegmatite 5-8.
Slip for producing glase coating / 2434818
Invention relates to glasing heat resistant ceramic tiles and stove tiles. The slip for obtaining glase coating contains the following in pts.wt: frit 100; clay 4-6; zircon 1-1.5; water 40-50; tin oxide 10-14; chamotte 6-8. The frit is prepared from the following components, pts.wt: clay 2-3; zircon 2-3; tin oxide 10-14; borax 10-14; quartz sand 68-74.
Method of production of electroinsulating glass enamel / 2453514
Frit of the following composition, wt % is melted: SiO2- 20.0-25.0; CaO- 4.5-12.0; SrO-1.0-2.0; CdO- 2.0-3.0; MnO- 0.1-0.5; K2O - 3.0-4.0; Na2O-1.0-1.5; B2O3- 5.0-5.5; CaF2-4.0-5.0; MoO3 - 0.5-0.8; Cr2O3 -0.5-0.8; Co2O3 -0.1-0.5; NiO - 0.1-1.0; Na3AlF6 - 0.1-0.5; BaO is the rest. Melting is carried out at 1150-1200 °C. The obtained product is crushed, and then injected 5-10% SrTiO3 of the frit weight.
Brown ceramic pigment / 2248333
Claimed pigment contains (mass %): Fe2O3 21.90-23.10; ZnO 33.04-38.56; SiO2 1.10-2.4; Al2O3 0.89-1.08; TiO2 9.30-11.01; CaO 0.99-1.14; MnO 1.04-1.20; MgO 0.40-0.62; K2O 0.24-0.36; FeO 22.70-27.00; Na2O 0.32-0.54; P2O5 0.21-0.41; V2O5 0.25-0.30. Titanomagnetite concentrate and zinc oxide are used as raw materials. Pigment composition of present invention makes it possible to reduce synthesis temperature up to 750-11000C and increase color purity up to 31.5-33.1 %.
Blend for preparing ceramic orange-brown-color pigment / 2255056
Invention concerns manufacture of ceramic pigments for decorating porcelain-faience and majolica articles. Blend for ceramic pigment contains SiO2, Al2O3, V2O5, and K2O in the form of baked diatomite-supported sulfovanadate catalyst composed of, wt %: SiO2 73.81, V2O5 8.33, Al2O3 5.95, K2O 11.91. Blend additionally contains 5-15% MnO. Synthesis temperature of pigment is 800-950°C. Pigment is recommended for use in overglaze ceramic paints and to color glazes.
|
FIELD: construction. SUBSTANCE: charge for glase production contains the following components, wt %: broken window sheet and/or container glass 76-82, kaolin 3-4, soda ash 1-2, zircon 8-11, pegmatite 5-8. EFFECT: improved frost resistance. 1 tbl
The invention relates to the technology of silicates and related compounds mixture for the preparation of glazes that can be used for application on exterior ceramic tile, brick, tile. Known charge to prepare the glaze, vkluchaysya, wt.%.: the battle window and/or glass containers 60-90; kaolin 5-20; at least one component from the group of sodium silicate, metasilicate sodium, soda ash, potassium hydroxide, water alkalis NaOH and KOH [1]. The objective of the invention is to increase the frost resistance obtained from charge glaze. The technical result is achieved by the fact that the charge for the preparation of glazes, including the breakage of the sheet and/or container glass, kaolin, soda ash, contains zircon and pegmatite in the following ratio, wt.%.: the breakage of the sheet and/or glass containers 76-82; kaolin 3-4; soda ash 1-2; zircon 8-11; pegmatite 5-8. The following table shows the composition of the glaze.
The glaze was obtained as follows. Prepare and dispense components according to the selected composition (table). Breakage of glass is washed from dirt, dry and grind to a complete pass through mesh No. 008. Zircon, pegmatite and kaolin grind to a complete pass through mesh No. 008. Milled components are mixed. To the resulting mass is added soda ash, water, and prepare the glaze slurry with a humidity of 45-55%. The prepared suspension is applied to the surface of ceramic products, dried and calcined at a temperature of 850-950°C. Sources of information 1. A.S. No. 773031 USSR, 1980. The charge for making the glaze, including the breakage of the sheet and/or container glass, kaolin, soda ash, characterized in that it contains zircon and pegmatite in the following ratio, wt.%:
|
|||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||