Water-dispersion paint

 

The invention relates to paints, varnishes and lacquers, and in particular to a water-dispersible compositions intended for internal finishing works in construction, for protective and decorative treatment of asbestos-cement, concrete, brick, wood and plaster surfaces. Water-dispersion paint contains 40,0-60,0 wt. % varnish, 1,00-18.0 wt.% metal oxide, 0.07 to 3.0 mass. % emulsifier and potassium salts of di-(alkylpolyglycoside) ester of phosphoric acid, 0.5 to 10.0 wt.% filler is 1.0-10.0 wt.% drying agent, 1.0 to 7.0 wt.% trichloropropane, or trichloracetate, or dibutyl phthalate, and the rest water. The filler may be a micro-talc, or kaolin, or their mixture, or a mixture of micro-talc or kaolin with a white soot. The ink may optionally contain a color pigment in an amount up to 16.0 wt.%. Water-dispersion paint has a high resistance and forms a glossy smooth or homogeneous type "orange peel" decorative film. 2 C.p. f-crystals, 2 tab.

Description text in facsimile form (see graphic part)

Claims

1. Water-dispersion paint containing a drying oil, a metal oxide, a filler, emulsifier, sikkat the first) ester of phosphoric acid and further comprises trichloropropylphosphate, or trichlorethylene, or dibutyl phthalate in the following ratio, wt.%.

Linseed oil 40,0-60,0

The metal oxide 1,00-18,0

The filler is 0.5 to 10.0

The above-mentioned emulsifier 0,07-3,0

Desiccant 1,0-10,0

Trichloropropylphosphate, or trichlorethylene, or dibutyl 1,0-7,0

Water the Rest

2. Paint on p. 1, wherein the filler contains a micro-talc, or kaolin, or their mixture, or a mixture of micro-talc or kaolin with a white soot.

3. The paint on each of p. 1 or 2, characterized in that it further comprises a color pigment in an amount up to 16.0 wt.%.

 

Same patents:

The invention relates to aqueous compositions for coatings containing 5 to 95 wt

The invention relates to materials having the ability to absorb active oxygen, and the use of these materials as a coating to the internal surfaces of containers, particularly cans

The invention relates to paint compositions, namely, primers, water-dispersion acrylic designed for priming and impregnating the walls of the facades and interior, including high humidity on concrete, aerated concrete, brick, stone, stucco surfaces, the surfaces of plasterboard, chipboard and fibreboard plates, and wooden surfaces before painting

The invention relates to aqueous coating composition containing a mixture of 90-99 wt.% composition of film-forming binder containing alkaline nanabhay dispersion type core-shell obtained by polyprionidae polymer (I), 1-10 wt.% modifying the rheological properties of dispersions obtained by polyprionidae polymer (II)

The invention relates to the field of construction, and more particularly to the construction composition used in interior and exterior design of buildings for industrial and civil use

The invention relates to the production of water-soluble acrylic paints for painting, decorative work, and fabric painting

The invention relates to woodworking, namely the technology of preparation of timber, mainly timber and thick boards (thickness up to 100 mm) before drying

The invention relates to the production of paint and varnish compositions, namely water-dispersion paints intended for interior and exterior painting of buildings and structures of brick, concrete, stucco, wood and other porous construction materials, old coatings

The invention relates to the production of the paint composition, namely a water-dispersible compositions intended for protection against atmospheric influences of various structural elements and components (panel and log walls, doors, frames, cornices, railings, and so on), saunas (except saunas), for the interior works (furniture, built-in cabinets, panels), as a finishing layer on mineral plasters, decorative brick

The invention relates to thermoplastic marking compositions
Sealant // 2208032
The invention relates to bodegasanmarcos.com chemicals, reversible hardening with the cured state of a certain elasticity, keeping it for a long time, so you can use it as a sealant at a temperature of from 100 to -50oWith

Artists oil colour // 2206587
The invention relates to a technology for artistic oil paints
The invention relates to compositions of the type emulsions of water and oil for impregnation of porous materials

The invention relates to a protective anti-corrosion compositions representing inhibited oil formulations intended for corrosion protection of surfaces of all kinds of vehicles

The invention relates to the production inhibited oil compositions for protection against corrosion

The invention relates to paint compositions used as coatings to protect metal and non-metal materials and products from them from biocorrosion lesions, and can be used in various industries

The invention relates to a water-wax protective structures against atmospheric exposure, aging, biodegradation of rubber, polymer, metal, wooden products and coatings

The invention relates to a process for the production of pigments and dispersing agents can be used in the paint industry in the manufacture of oil paints for exterior and interior works

FIELD: corrosion protection.

SUBSTANCE: invention is designed for oil production and can also be used in mechanical engineering, instrumentation engineering, and other branches. Composition contains 6-10% low-grade lignosulfonates, 2-5% industrial oil (spindle oil, tall oil, or MS-20 oil), 60-65% production waste, and 24-28% additive, namely primary C8-C11-amines. Production waste is, in particular, vat residues from production of synthetic fatty C10-C-acids or solid petroleum hydrocarbons: asphaltene-tar-paraffin deposits formed during production and transportation of petroleum. Use of composition increases degree of protection of metallic objects against corrosion under atmospheric precipitate conditions owing to retained high adhesion of coating formed from composition to metal, reduced porosity of coating, and prolonged period of time before appearance of the first center of corrosion attack at lower thickness of coating.

EFFECT: improved anticorrosion characteristics, simplified composition preparation technology, reduced coating formation time, and reduced expenses due to utilized waste.

2 cl, 2 tbl

Up!