Method to produce fuel briquettes

FIELD: power engineering.

SUBSTANCE: invention includes mixing of ground solid fuel with a binder, briquetting of the mix under pressure, where the ground solid fuel is coke dust with particle size of less than 1 mm, and the binder is coking sludge in the amount of 8.0-10% to the weight of coke dust, the die mould is first heated to 40-50°C, and briquetting of the mix under pressure is carried out under pressure in stages, for this purpose they first set load of 5-6 atm, with a delay of 3-5 min and then up to 15 atm with delay at maximum load of 3-5 min. The produced briquettes maybe used as fuel for burning in domestic and industrial furnaces, as well as for coking in chemical-recovery and metallurgical industry.

EFFECT: production of fuel briquettes of higher strength, improved environmental situation in coal processing regions, reduced prime cost of fuel briquettes.

2 tbl, 3 ex

 

The invention relates to the technology of briquetting combustible components, such as coal slurries, small classes of coal, coke dust, etc. these briquettes can be used as fuel for combustion in domestic and industrial furnaces, as well as for coking in the coking and metallurgical industries.

The problem of utilization of coke dust coke enterprises is very important. The production of coke dust are very high, on average, one coke company annually produces about 18-20 tonnes of coke dust. The use of coke dust practically does not find due to the finely dispersed state and a high ash content, the difficulty of unloading and transportation.

The invention contributes to the solution of environmental problems associated with the formation and disposal of waste by-product coke plants (coke dust, fusou coking).

Known methods of producing fuel briquettes from coals and anthracites, including dehydration and drying of raw coal to a moisture content of 2-3%, mixing it with liquid or solid binder (bitumen, coal tar pitch, sulfate distillery stillage, solid clay, cement), compressing the mixture pressure of 20-50 MPa, and then cool (see he was the A.T. "briquetting of minerals", M: "EDR", 1989, p.86, 92, 98, 101, 106).

The above methods have the following disadvantages:

First, the need for the proposed use of the binder greatly complicates and increases the cost of the process of briquetting coal, because it provides for operation deep dewatering and thermal drying of raw coal to the minimum values for humidity, i.e. up to 2-3%.

Secondly, the existing technology of briquetting coals and anthracites are not intended for use as a feedstock coke dust (class size 0-1,0 mm) and fine coal slurries (class size 0-1,0 mm)from the mining and processing of coal. Coal sludge and coke dust is discharged into settling tanks and dumps coal processing enterprises, which degrades the ecological state of the environment in coal mining regions.

Closest to the proposed invention by the technical nature (prototype) is a method of producing fuel briquettes, comprising mixing the crushed solid fuel on the basis of coke breeze with particle sizes of 0.05-16,0 mm in the amount of 50-80 wt.% binders based on modified lignosulfonate in the number of 8-9% by weight of the crushed solid fuel briquetting mixture under a pressure of 25 MPa and a subsequent heat treatment of the briquettes (Patent P is No. 2298028, publ. 27.04.2007,).

There is a method of producing fuel briquettes has the following disadvantages:

1. High pressure (25 MPa), which is economically and energetically unprofitable and technically difficult to achieve.

2. Coke breeze itself is a commodity product. Coke breeze serves as fuel for various industrial plants, is used for agglomeration of iron, Nickel ores, the manufacture of electrodes.

Proposed briquetting coke dust, which is a high-calorie waste by-product coke enterprises.

The technical result of the claimed invention to provide a fuel briquettes of high strength, made from coke dust and fusou coking, which will improve the ecological situation in the processing regions, to reduce the cost of fuel briquettes.

The technical result is achieved in that in the method of producing fuel briquettes, comprising mixing powdered solid fuel and binder, briquetting the mixture under pressure, according to the invention, as the crushed solid fuel use coke dust with particle sizes less than 1 mm, as a binder used by fuse coking in the amount of 8.0 to 10% by mass of coke dust, mold pre-heated to a temperature 40-0°C, briquetting the mixture under pressure to produce speed, which initially set load 5-6 ATM, aged 3-5 min and further to 15 ATM. with tenacity at maximum load 3-5 minutes

The inventive method is as follows.

Coke dust is mixed with a binder component (FUS coking) in percentage ratio of 92:8, and the mixture is then loaded into the system, consisting of the mold, the heating element and thermometer showing the temperature of the mold. All of these elements obsolescene thermohousing. The mold is pre-heated to 40-50°C. the resulting mixture was pressed into stamp press step: first set the load 5-6 ATM aged 3-5 min and further to 15 ATM with shutter speed at maximum load 3-5 minutes At speed pressing optimum interaction of components in a mixture, with formation of the structure of the fuel briquette.

Choice as a binder fusou coking due to their availability. Fuse coking is waste coal production during coking. They are represented by 50% resins heavy fractions and solid carbonaceous inclusions. Fuse coking and coke dust as a waste by-product coke plants, can be used directly to these same companies.

The binder consumption (fusou coking) is predelay need for the formation of a solid fuel briquette.

Get a fuel briquettes with the following technical characteristics (table 1).

Table 1
Technical characteristics of the resulting briquettes
Physical testingFuel characteristics
compression, kg/cm2abrasion, % content pieces the size of >25 mmflushing, % content pieces the size of >25 mmAd, % wt. (ash)Qsrkcal/kg (heat of combustion)Stdwt.%. (sulfur content)
50-6094926,495000,05

An example of a specific application of the method.

Take 92 g of coke dust and mixed with 8 g fusou coking to visual mixing./p>

The resulting mixture is loaded into the experimental setup, consisting of the mold, the heating element and thermometer showing the temperature of the mold. The mold is pre-heated to 50°C. the resulting mixture was pressed into stamp press step: first set the load 5 ATM, aged 3 min and further to 15 ATM with shutter speed at maximum load 5 minutes

Get a fuel briquettes suitable for coking and direct combustion, technical characteristics are presented in table 2.

Table 2
Technical characteristics of the resulting briquettes
Physical testingFuel characteristics
compression, kg/cm2abrasion, % content pieces the size of >25 mmflushing, % content pieces the size of >25 mmAd, % wt. (ash)Qsrkcal/kg (heat of combustion) Std% wt, (sulfur content)
6094926,495000,05

Example 2.

Take 92 g of coke dust and mixed with 8 g fusou coking to visual mixing.

The resulting mixture is loaded into the experimental setup, consisting of the mold, the heating element and thermometer showing the temperature of the mold. The mold is pre-heated to 50°C.

The resulting mixture is pressed into stamp press with a load of 5 ATM 5 minutes

The output is not getting fuel briquettes as lower compaction pressure of less than 15 ATM reduces the strength of the fuel briquette.

Example 3.

Take 85 g of coke dust and mixed with 15 g of fusou coking to visual mixing.

The resulting mixture is loaded into the experimental setup, consisting of the mold, the heating element and thermometer showing the temperature of the mold. The mold is pre-heated to 50°C.

The resulting mixture is pressed into stamp press with a load of 25 MPa 5 minutes

The output is not getting fuel briquettes as:

1. According to the mathematical is Oh dependencies designed by Dr. A.T.-he was, involving more than 10% of the binding reagent in the system is economically and technologically justified.

2. Use a sharp increase in pressure up to 25 MPa results in unstable fuel briquettes due to the inhomogeneous distribution of the binder by weight of the concentrate.

The proposed method of producing fuel briquettes can improve the durability of fuel briquettes and lower their costs. In the proposed method for the production of fuel briquettes are used coke dust and fuse coking, which is a waste by-product coke plants, disposal of these wastes which will improve the ecological situation in the coal refining regions.

Method of producing fuel briquettes, comprising mixing powdered solid fuel and binder, briquetting the mixture under pressure, characterized in that as the crushed solid fuel use coke dust with particle sizes less than 1 mm, as a binder used by fuse coking in the amount of 8.0 to 10% by mass of coke dust, mold pre-heated to a temperature of 40-50°C, briquetting the mixture under pressure to produce speed, which initially set load 5-6 ATM, aged 3-5 min and further to 15 ATM with shutter speed at the maximum loading is ke 3-5 minutes



 

Same patents:

FIELD: power engineering.

SUBSTANCE: invention includes mixing of ground solid fuel with a binder, briquetting of the mixture under pressure, where the ground solid fuel is coke dust with particle size of less than 1 mm, and the binder is coking sludge in the amount of 8.0-10% to the weight of coke dust, the mixture of coke dust and the binder is heated to 100°C, pressed in stages: first the load of 5-6 atm is set with a delay of 3-5 min and then up to 15 atm with a delay at the maximum load for 3-5 min, the finished fuel briquette is tempered at 250-300°C without access of air for 10-12 min. The produced briquettes may be used as fuel for combustion in domestic and industrial furnaces, and also for coking in chemical-recovery and metallurgical industry.

EFFECT: production of smokeless fuel briquettes of higher strength, improved environmental situation in coal processing regions, reduced prime cost of fuel briquettes.

2 tbl, 3 ex

FIELD: oil and gas industry.

SUBSTANCE: method for production of formed coke of carbon-containing material includes stages of oil semi-coke heating, pressure moulding with obtainment of green mouldings and their further cocking. Oil semi-coke is heated up to 350-400°C, at that oil semi-coke with carbon-to-hydrogen atomic ratio within range of (1.3-1.7) or oil semi-coke with carbon-to-hydrogen atomic ratio more than 1.7 is used with addition of sintering additives. After the heating stage before moulding the heated oil semi-coke is hold within 10-20 s.

EFFECT: invention allows improving quality of mouldings, simplifying the method and increasing technology stability and reliability, reducing energy costs and expanding sources of raw materials.

3 cl, 2 dwg, 1 tbl, 4 ex

FIELD: chemistry.

SUBSTANCE: method involves thermal treatment of low-grade fuel at temperature 200-500°C. A pyrolysis product is obtained - low-temperature pyrolysis resin and a carbon residue. The carbon residue is crushed and mixed with low-temperature pyrolysis resin in equal parts. Briquettes are moulded from the obtained mixture. The briquettes are dried at temperature not higher than 200°C. The obtained fuel briquettes are left to solidify at room temperature for one day.

EFFECT: minimising processing equipment used.

1 cl, 5 ex, 1 dwg

FIELD: manufacture of building materials.

SUBSTANCE: invention relates to manufacture of molded fuel, in particular to fabrication of high-carbon fuel briquettes, which can be used when smelting cast iron in cupola-furnaces, when producing calcium carbide, silicon carbide, mineral fibers, and other materials. Process according to invention comprises mixing ground solid fuel with binder in amount 5-9% of the weight of ground solid fuel and briquetting mix followed by heat treatment of briquettes. Ground solid fuel is composed of coke fines with particle size 0.05-16.0 mm, 50-80%, and thermoantracite fines with particle size 0.05-6.0 mm, 20-50%. Binder is lignosulfonates modified with 3-5% of petroleum or petroleum products. Briquetting of mix is effected under pressure 25 MPa.

EFFECT: reduced power consumption, investment and operational expenses, increased briquette fabrication productivity, and increased strength, heat resistance, and calorific value of fuel briquettes.

3 ex

FIELD: solid fuel technology.

SUBSTANCE: invention is designed for application in production of solid fuel in metallurgy and for domestic necessities. Method of restoring sieve composition of coke comprises mixing off-grad coke with binder, such as various cement brands and Portland cement, moistening, briquetting of mix followed by heat treatment, and cooling. Off-grad coke utilized is coke fines fraction 0-10 mm and/or coke nut fraction 10-25 mm belonging to a certain types, which are mixed with binder at ratio (60-95):(5-40), respectively. Moistening is provided by adding water to 35% based on the weight of mix. Heat treatment is effected with steam. Cooling proceeds at ambient temperature to residual moisture content 5%. Mix is completed with filler in the form of organic or inorganic naturally occurring or man-made substances. Briquetting is effected on either vibration or press equipment. Coke briquette contains 60 to 95% of above-defined off-grade coke and 5 to 40 % of binder. Size of thus manufactured briquettes corresponds to required sieve composition of coke.

EFFECT: enabled full restoration of all fractions of needless process coke residues to useful sieve composition appropriate for fabrication of environmentally safe briquettes with improved consumer's properties without considerable investments.

8 cl, 1 tbl, 6 ex

FIELD: production of solid carbonaceous fuel.

SUBSTANCE: the invention is pertaining to the method of production of solid fuel briquettes and may be used at enterprises producing a household fuel. The method provides for mixing of slack coal (sludge cake) with the diameter of fragments of 0.05-0 mm with a mass share a moisture of 16-17 % and with 5 % (23-34 %) of water solution of a cationic polyelectrolyte, compaction of a charge mixture by a hydraulic press at the pressure of 340 kg/cm2 and the thermal treatment at the temperature of t=150°C within 30 minutes. The invention allows to reduce pollutants emissions into the aerosphere at incineration of the solid fuel briquettes that reduces the negative effect on the natural environment and also to exclude the usage of an expensive undersized coke.

EFFECT: the invention ensures reduction of the contaminants emissions into the aerosphere at incineration of the solid fuel briquettes and reduction of the negative effect on the natural environment and also to exclude the usage of the expensive undersized coke.

3 tbl

The invention relates to the production process fuel for use in mining and roasting processes
The invention relates to the technology of production of briquetted fuel and can be used for household needs, metallurgical and chemical industries
The invention relates to the technology of briquetting coke breeze, coke dust and sludge, in particular the production of coke briquettes

FIELD: power engineering.

SUBSTANCE: invention includes mixing of ground solid fuel with a binder, briquetting of the mixture under pressure, where the ground solid fuel is coke dust with particle size of less than 1 mm, and the binder is coking sludge in the amount of 8.0-10% to the weight of coke dust, the mixture of coke dust and the binder is heated to 100°C, pressed in stages: first the load of 5-6 atm is set with a delay of 3-5 min and then up to 15 atm with a delay at the maximum load for 3-5 min, the finished fuel briquette is tempered at 250-300°C without access of air for 10-12 min. The produced briquettes may be used as fuel for combustion in domestic and industrial furnaces, and also for coking in chemical-recovery and metallurgical industry.

EFFECT: production of smokeless fuel briquettes of higher strength, improved environmental situation in coal processing regions, reduced prime cost of fuel briquettes.

2 tbl, 3 ex

FIELD: power engineering.

SUBSTANCE: invention relates to a device for briquetting of biowaste of animals and birds, comprising a loading hopper, a conical auger installed in the hollow body, a scraper conveyor arranged in the lower part of the body, a spring-loaded plate in the form of a ski is installed at the side of the conical auger top at the outlet from the body. It additionally comprises a mixer made of a body, nozzles for input of a filler and an aggregate, besides, along the vertical axis of the mixer body there is a rotor with blades arranged at the angle to each other, the lower part of the mixer via the gate and the pipeline is connected to the lower part of the device for mixing of the material with the binder made of a body and a nozzle of binder injection, inside the body on its opposite sides there are two augers in the form of a spiral with the opposite winding rotating with the help of electric motors, at the outer side of the device body for mixing along its perimeter there is a coil with a coolant. Blades installed on the rotor of the mixer have the shape of a rectangular triangle. Application of the proposed device makes it possible to use biowaste of animals (manure, dung), and also to use local resource in the form of easily available and environment-safe materials.

EFFECT: produced briquettes are used for heat production.

2 cl, 1 dwg

FIELD: chemistry.

SUBSTANCE: briquette consists of a pressed lignocellulose body, containing: (a) 60-90 wt % cuttings of grass stalks and (b) 10-40 wt % scutched lignocellulose binder with degree of scutching of 38-75°RS (Shopper-Rigler degrees), preferably 45 70°RS, (said percentages being expressed in dry weight relative the dry weight of the sum of (a) and (b)) and from fuel which is liquid at room temperature, having a flash point of 30-150°C, which saturates the pressed lignocellulose body, wherein said briquette has a substantially cylindrical shape and has a central smoke conduit with a star-shaped cross-section. The method of making the briquettes comprises the following steps: (1) mixing an aqueous suspension of lignocellulose binder (b) with cuttings of grass stalks (a) in such proportions that the ratio (per dry weight) of the lignocellulose binder (b) to the cuttings of the grass stalks (a) ranges from 10/90 to 40/60; (2) moulding the mixture obtained in a suitable unit of the mould (encircling part)-anti-mould (encircled part) type at temperature of 40-120°C at pressure of 3-12 bar, applied for 5-120 s; (3) removing the obtained pressed body from the press mould; and (4) saturating the pressed body removed from the press mould with fuel which is liquid at room temperature, having flash point of 30-150°C.

EFFECT: obtaining a solid fuel briquette with low weight and a shape which provides multiple points of ignition, concealed inside the central smoke conduit.

15 cl, 3 dwg

FIELD: chemistry.

SUBSTANCE: method of making fuel briquettes involves grinding combustible solid components, mixing with binder, pressing and drying the briquettes. The method is characterised by that the combustible solid components used are recycled ballistit-type gun powder or non-recoverable wastes from powder production, ground on a modernised disk mill to particle size of 0.5-1.0 mm, and activated charcoal screenings, ground on a double-roll crusher to particle size of less than 4.0 mm, and mixed in 8.0-10.0% aqueous solution of polyacrylamide binder or a sodium salt of carboxymethyl cellulose in a continuous or periodic action mixing device with horizontal mixers, followed by pressing into fuel briquettes on a shaft pelleting press; the formed briquettes are dried with air on a three-section belt drier at temperature 100…105°C for 3 hours, cooled and then dry-cured for three days.

EFFECT: wider raw material base for making fuel briquettes, environmentally safe recycling of discarded gun powder, ballistit wastes and activated charcoal screenings not suitable for use as an adsorbent, high energy output and calorific capacity of the fuel briquettes.

1 dwg, 2 ex

FIELD: chemistry.

SUBSTANCE: invention relates to briquetted solid fuel, which contains activated charcoal screenings and ballistit powder wastes which do not contain heavy metal salts and other environmentally hazardous components, ground to particle size of 0.5-1.0 mm, and polyacrylamide as binder, with the following ratio of components, wt %: activated charcoal screenings - 75…86, ballistit powder wastes - 10…20, polyacrylamide - 4…5. The invention enables to comprehensively solve the problem of the environment, saving energy resources and recycling potentially hazardous high-energy substances.

EFFECT: solid fuel has higher flammability, low ash content and high calorific capacity.

1 tbl

FIELD: chemistry.

SUBSTANCE: briquetted solid fuel contains activated charcoal screenings and expired ballistit powder, ground to particle size of 0.5-1.0 mm, and polyacrylamide as binder, with the following ratio of components, wt %: activated charcoal screenings - 75…86, expired ballistit powder - 10…20, polyacrylamide - 4…5.

EFFECT: fuel has high calorific capacity, high flammability coupled with low ash content and satisfactory mechanical properties of the briquetted solid fuel during use.

1 tbl

FIELD: oil and gas industry.

SUBSTANCE: invention relates to a method of making fuel briquettes from biomass, involving heat treatment of biomass at temperature of 200-500°C without access to air, preparing binding substance obtained by dissolving dextrin in a pyrolysis condensate in ratio of 1:(5-20), mixing the binder with a carbon residue ground to particle size of 2 mm, moulding a fuel briquette from the obtained mixture and drying said briquette at room temperature for 2-5 days. The obtained briquettes have low combustion heat, improved mechanical strength and resistance to compression.

EFFECT: use of the disclosed method widens the range of solid fuel, the raw material base for making briquettes and reduces technological expenses on making briquettes.

1 cl, 1 dwg, 1 tbl, 6 ex

FIELD: chemistry.

SUBSTANCE: invention relates to producing efficient briquetted solid fuel for household heating ovens, fireplaces, heating devices for hot water supply and gas powered electric generators. Described is briquetted solid fuel which contains activated charcoal screenings and ballistit powder ground to particle size of 0.5-1.0 mm, and the binder used is polyacrylamide, with the following ratio of components, wt %: activated charcoal screenings 75-86, ballistit powder 10-20, binder 4-5.

EFFECT: invention enables to simultaneously solve problems relating to the environment, resource saving and recycling potentially hazardous high-energy components.

1 tbl

FIELD: power engineering.

SUBSTANCE: method to produce briquette fuel includes stages for preparation of initial components, mixing, pressing and drying. Components used are a carbon-containing material, such brown coal medium-temperature coke of the initial grain-size composition, a mineral binder, such as subcoal aleurolite, a strengthening modifier, such a 3% aqueous solution of a polyvinyl alcohol (PVA) or an aqueous solution of 10% flour paste, a hydrophobe modifier, such as fuel oil of M100 grade and water, at the following ratio of components, wt %: mineral binder - 1-10; strengthening modifier - 1-30; hydrophobe modifier - 1-10; water - 1-30; carbon-containing material - balance. After mixing of components the briquette mass is pressed into briquettes under pressure of 20-200 MPa, and then briquettes are dried at the temperature 100-250°C.

EFFECT: method improvement.

4 cl, 15 ex

FIELD: power engineering.

SUBSTANCE: invention relates to the method for production of coal briquettes from coal slurry and coal fines with a binder - an aqueous solution of polyelectrolyte - a flocculant on the basis of a polyacrylamide (PAA). As an intensifying additive to increase adhesion as a charge is compressed in process of pressing, the initial solution of PAA is complemented with water-soluble surfactants from the class of polyethers based on propylene glycol. Coal briquettes are used for communal-domestic and technological purposes.

EFFECT: higher efficiency of application.

FIELD: power engineering.

SUBSTANCE: invention includes mixing of ground solid fuel with a binder, briquetting of the mixture under pressure, where the ground solid fuel is coke dust with particle size of less than 1 mm, and the binder is coking sludge in the amount of 8.0-10% to the weight of coke dust, the mixture of coke dust and the binder is heated to 100°C, pressed in stages: first the load of 5-6 atm is set with a delay of 3-5 min and then up to 15 atm with a delay at the maximum load for 3-5 min, the finished fuel briquette is tempered at 250-300°C without access of air for 10-12 min. The produced briquettes may be used as fuel for combustion in domestic and industrial furnaces, and also for coking in chemical-recovery and metallurgical industry.

EFFECT: production of smokeless fuel briquettes of higher strength, improved environmental situation in coal processing regions, reduced prime cost of fuel briquettes.

2 tbl, 3 ex

Up!